氧化铝陶瓷广泛用作研磨材，切削材、高温材料，加之具有良好的耐磨蚀性、机械强度、硬度和耐磨性，还用于各种机械部件。但原用氧化铝陶瓷由于无塑性，不能像金属材料那样进行加工，可以说属一种很难加工的材料。
这种陶瓷是在高分子中电解质水溶液中分散AI2O3和Zr2O3颗粒，制备料浆，注入多孔质模，加压成坯，加热烧结而成。由于它是一种含有Zr2O3的氧化铝结拼烧结体，Zr2O3氧化铝颗粒处于高分散状态，且结晶呈微细粒，具有良好的超塑性。
经测定，在1400℃和1500℃下，以1mm/min的速度进行拉伸形试验，其测定值超过200%。由于它弥补了原有氧化铝陶瓷无塑性的缺陷，使其用途得到进一步拓宽。（图/文www.cddnvga.cn）
中译英：
Alumina ceramics are widely used as grinding materials, cutting material, high temperature materials, and has good abrasion resistance, mechanical strength, hardness and wear resistance, is also used in a variety of mechanical parts. But the original alumina ceramic because no plastic, not metal materials such as processing, can be said to belong to a kind of difficult to machining materials.

The ceramic is in polymer electrolyte aqueous dispersions of AI2O3 and Zr2O3 particles, preparation of slurry, into the porous mold, compression casting, heating sintering. Because it is a Zr2O3 containing the alumina sintered body knot together, Zr2O3 alumina particles at high dispersion state, and the crystallization is fine, has good superplasticity.